92 micrographs available, ordered by micrograph number.
Showing 41 - 50 of 92 micrographs | Page 1 2 3 4 5 6 7 8 .. 10 | Previous | Next |
Micrograph
193
:
MgO-C Refractory Brick System: MgO-C, Composition: MgO 50-90, C 8-37 (wt%), remainder Al, Si metal addition Reflected light microscopy 200 μm |
|
Micrograph
194
:
MgO-C Refractory Brick System: MgO-C, Composition: MgO 50-90, C 8-37 (wt%), remainder Al, Si metal addition Reflected light microscopy 200 μm |
|
Micrograph
195
:
Zirconia Toughened Alumina (ZTA) System: ZrO2-Al2O3, Composition: ZrO2 5-30, Al2O3 70-95 (wt%) Scanning electron microscopy (SEM) in backscattered electron imaging (BEI) mode 10 μm |
|
Micrograph
196
:
Tetragonal Zirconia Polycrystals (TZP) System: ZrO2-Y2O3, Composition: Y2O3 2-3, ZrO2 96-97 (wt%) Bright-field TEM 600 nm |
|
Micrograph
197
:
Partially Stabilised Zirconia (PSZ) System: ZrO2-MgO, Composition: MgO 2.5-3.6, ZrO2 97.5-96.4 (wt%) Bright-field TEM 300 nm |
|
Micrograph
198
:
96% Alumina System: Al2O3, Composition: Al2O3 96%, remainder MgO, CaO, SiO2 Reflected light microscopy 250 μm |
|
Micrograph
199
:
BaTiO3 Temperature-stable dielectric capacitor System: BaTiO3 + other oxides such as Nb2O5, Bi2O3, Composition: BaTiO3 95-97 (wt%) Bright-field TEM 1 μm |
|
Micrograph
542
:
Devitrified Glass: glass sample heated at 900°C for 17 hours. System: SiO2, Composition: Mostly silica, SiO2 Transmitted polarised light microscopy, with sensitive tint plate 100 μm |
|
Micrograph
543
:
Devitrified Glass: glass sample heated at 900°C for 17 hours System: SiO2, Composition: Mostly silica, SiO2 Transmitted polarised light microscopy, with sensitive tint plate 250 μm |
|
Micrograph
544
:
Devitrified Glass: glass sample heated at 900°C for 17 hours System: SiO2, Composition: Mostly silica, SiO2 Transmitted polarised light microscopy, with sensitive tint plate 250 μm |