708 micrographs for category Metal or alloy:
Showing 581 - 590 of 708 micrographs | Page 1 .. 56 57 58 59 60 61 62 .. 71 | Previous | Next |
Micrograph
831
:
Austenitic stainless steel water quenched, with a-martensite needles within lamellae System: Fe-C-X, Composition: Fe, C 0.12, Mn 14.2, Cr 13.7 Scanning electron microscopy (SEM) 4 μm |
|
Micrograph
832
:
Austenitic stainless steel tempered System: Fe-C-X, Composition: Fe, C 0.2, Mo 4 (wt%) Transmission electron microscopy (TEM) 200 nm |
|
Micrograph
833
:
Austenitic stainless steel solution treated, quenched then tempered System: Fe-C-X, Composition: Stainless steel with Cr 18, Ni 10, Nb 1 (wt%) Reflected light microscopy 50 μm |
|
Micrograph
834
:
Steel slowly cooled, fracture surface of commercial ingot System: Fe-C-X, Composition: Fe, C 0.13, Ni 4, Cr 2, Mn 0.49, S 0.015 (wt%) Scanning electron microscopy (SEM) 4 μm |
|
Micrograph
835
:
Martensitic steel tempered, with precipitation of Mo2C System: Fe-C-X, Composition: Fe, C 0.2, Mo 4 (wt%) Transmission electron microscopy (TEM) 1 μm |
|
Micrograph
841
:
Micrograph of base material microstructure: H32 - cold-worked and stabilised to obtain 1/4 hardness. System: Al-Mg, Composition: Al, Mg 4.5, Mn 0.7 (wt%) Optical microscope, interferential contrast 100 μm |
|
Micrograph
842
:
Macrograph of a resistance spot weld made in two plates of 1,5mm thickness. T3 - solution heat treatment, cold working and natural ageing. System: Al-Cu, Composition: Al, Cu 4.5, Mg 1.5 (wt%) Optical microscope, interferential contrast 1 mm |
|
Micrograph
843
:
Micrograph of base metal. T6 - solution heat treated and artificially aged. System: Al-Mg-Si, Composition: Al, Mg 1, Si 0.8, Mn 0.5 (wt%) Optical microscope, reflected light 250 μm |
|
Micrograph
844
:
Microstructure of extruded tube in Magnesium alloy AZ91 in direction perpendicular to the direction of extrusion. System: Mg-Al, Composition: Mg, Al 9.2, Zn 0.8 (wt %) Optical microscope, reflected light 500 μm |
|
Micrograph
845
:
Microstructure of extruded tube in Magnesium alloy AZ91 in direction perpendicular to the direction of extrusion. System: Mg-Al, Composition: Mg, Al 9.2, Zn 0.8 (wt %) Optical microscope, reflected light 50 μm |
Showing 581 - 590 of 708 micrographs | Page 1 .. 56 57 58 59 60 61 62 .. 71 | Previous | Next |