Category
708 micrographs for category Metal or alloy:
| Showing 71 - 80 of 708 micrographs | Page 1 .. 5 6 7 8 9 10 11 .. 71 | Previous | Next |
 |
Micrograph
71
:
Silal System: Fe-C-X, Composition: Fe, C 3.0, Si 6, Mn 0.7, P 0.3, S 0.1 (wt% typical) (Silal) Reflected light microscopy 80 μm |
 |
Micrograph
72
:
Ni-hard iron System: Fe-C-X, Composition: Fe, C 2.8, Ni 4.5, Mn 1.2, Cr 0.75, Si 0.5, P 0.3, Mo 0.25, S 0.1 (wt% typical) (Ni-hard iron) Reflected light microscopy 400 μm |
 |
Micrograph
73
:
Ni-hard iron System: Fe-C-X, Composition: Fe, C 2.8, Ni 4.5, Mn 1.2, Cr 0.75, Si 0.5, P 0.3, Mo 0.25, S 0.1 (wt% typical) (Ni-hard iron) Reflected light microscopy 80 μm |
 |
Micrograph
75
:
Notched zinc, broken by impact at room temperature System: Zn, Composition: Notched zinc Scanning electron microscopy (SEM) 1 mm |
 |
Micrograph
76
:
Notched zinc, broken by impact at room temperature System: Zn, Composition: Notched zinc Scanning electron microscopy (SEM) 160 μm |
 |
Micrograph
78
:
Forging steel, brittle, intergranular fracture System: Fe-C-X, Composition: Forging steel Scanning electron microscopy (SEM) 800 μm |
 |
Micrograph
79
:
Ni-superalloy, fatigue crack propagation System: Ni-X, Composition: Not specified (Ni-Superalloy) Scanning electron microscopy (SEM) 150 μm |
 |
Micrograph
80
:
Ni-superalloy, fatigue crack propagation System: Ni-X, Composition: Not specified (Ni-Superalloy) Scanning electron microscopy (SEM) 80 μm |
 |
Micrograph
81
:
Ni-superalloy, fatigue crack propagation System: Ni-X, Composition: Not specified (Ni-Superalloy) Scanning electron microscopy (SEM) 30 μm |
 |
Micrograph
82
:
Aluminium, fracture surface System: Al, Composition: Not specified Scanning electron microscopy (SEM) 15 μm |
| Showing 71 - 80 of 708 micrographs | Page 1 .. 5 6 7 8 9 10 11 .. 71 | Previous | Next |