Micrograph Library
Browse the libraryAdvanced searchSystemsCompositionsTechniquesKeywordsPhase diagramsHelpPreferencesAbout the micrograph libraryTerms of useContribute micrographs!FeedbackLinksCredits Print this page
Category
74 micrographs for category Polymer:
| Showing 1 - 10 of 74 micrographs | Page 1 2 3 4 5 6 7 8 | Previous | Next |
 |
Micrograph
114
:
Poly (lactic-co-glycolic acid) (PLGA) porous scaffold for tissue engineering. Average Pore Size 350-550 micrometre, porosity estimated at 35-45% System: Poly (lactic-co-glycolic acid) (PLGA), Composition: Not specified Scanning electron microscopy (SEM) 3 mm |
 |
Micrograph
115
:
Poly (lactic-co-glycolic acid) (PLGA) porous scaffold for tissue engineering. Average Pore Size 350-550 micrometre, porosity estimated at 35-45% System: Poly (lactic-co-glycolic acid) (PLGA), Composition: Not specified Scanning electron microscopy (SEM) 250 μm |
 |
Micrograph
116
:
Poly (lactic-co-glycolic acid) (PLGA) porous scaffold for tissue engineering. Enlargement of a Pore. Average Pore Size 350-550 mm, porosity estimated at 35-45% System: Poly (lactic-co-glycolic acid) (PLGA), Composition: Not specified Scanning electron microscopy (SEM) 250 μm |
 |
Micrograph
118
:
Poly (lactic-co-glycolic acid) (PLGA) porous scaffold for tissue engineering. Average Pore Size 100-300 µm, porosity estimated at 65% System: Poly (lactic-co-glycolic acid) (PLGA), Composition: Not specified Scanning electron microscopy, environmental 400 μm |
 |
Micrograph
555
:
Banded spherulites in a blend of polyethtylenes System: Polyethylene (PE), Composition: LPE:BPE 1:3 Transmission electron microscopy (TEM) 200 nm |
 |
Micrograph
556
:
Sheaf-like arrangement of lamellae in a blend of polyethylenes System: Polyethylene (PE), Composition: LPE:BPE 3:1 Transmission electron microscopy (TEM) 200 nm |
 |
Micrograph
557
:
High Impact Polystyrene (HIPS) System: High Impact Polystyrene (HIPS), Composition: PS - 15%PB Transmitted light microscopy 10 μm |
 |
Micrograph
558
:
High Impact Polystyrene (HIPS) System: High Impact Polystyrene (HIPS), Composition: PS - 35%PB Transmitted light microscopy 20 μm |
 |
Micrograph
559
:
Shear bands in stressed polycarbonate System: Polycarbonate (PC), Composition: Not specified Scanning electron microscopy (SEM) 800 μm |
 |
Micrograph
560
:
Crazing near a fracture surface in polystyrene System: Polystyrene (PS), Composition: Not specified Photography (no microscope) 10 mm |
| Showing 1 - 10 of 74 micrographs | Page 1 2 3 4 5 6 7 8 | Previous | Next |