Composition
6 micrographs for composition Not specified (System: Si3N4-SiC composite), ordered by micrograph number.
![]() |
Micrograph
546
:
Delamination cracks seen in h-BN particles subjected to compressive stress in the (0001) planes (within a silicon nitride particulate-reinforced silicon carbide composite) System: Si3N4-SiC composite, Composition: Not specified High resolution electron microscopy (HREM) 10 nm |
![]() |
Micrograph
547
:
h-BN inclusion (precipitate) in a b-Si3N4 grain (within a silicon nitride particulate-reinforced silicon carbide composite) System: Si3N4-SiC composite, Composition: Not specified High resolution electron microscopy (HREM) 20 nm |
![]() |
Micrograph
549
:
Misoriented interphase boundary between h-BN (precipitate) and SiC grains (within a silicon nitride particulate-reinforced silicon carbide composite) System: Si3N4-SiC composite, Composition: Not specified High resolution electron microscopy (HREM) 1.2 nm |
![]() |
Micrograph
551
:
A regularly stepped interface boundary between h-BN (precipitate) and Si3N4 grains (within a silicon nitride particulate-reinforced silicon carbide composite) System: Si3N4-SiC composite, Composition: Not specified High resolution electron microscopy (HREM) 10 nm |
![]() |
Micrograph
552
:
An amorphous phase trapped at a triple junction between Si3N4 grains (within a silicon nitride particulate-reinforced silicon carbide composite). System: Si3N4-SiC composite, Composition: Not specified High resolution electron microscopy (HREM) 20 nm |
![]() |
Micrograph
553
:
Image of part of a crystalline triple junction between SiC grains (within a silicon nitride particulate-reinforced silicon carbide composite) System: Si3N4-SiC composite, Composition: Not specified High resolution electron microscopy (HREM) 6 nm |