Contributor
5 micrographs contributed by V A Mellon, ordered by micrograph number.
![]() |
Micrograph
114
:
Poly (lactic-co-glycolic acid) (PLGA) porous scaffold for tissue engineering. Average Pore Size 350-550 micrometre, porosity estimated at 35-45% System: Poly (lactic-co-glycolic acid) (PLGA), Composition: Not specified Scanning electron microscopy (SEM) 3 mm |
![]() |
Micrograph
115
:
Poly (lactic-co-glycolic acid) (PLGA) porous scaffold for tissue engineering. Average Pore Size 350-550 micrometre, porosity estimated at 35-45% System: Poly (lactic-co-glycolic acid) (PLGA), Composition: Not specified Scanning electron microscopy (SEM) 250 μm |
![]() |
Micrograph
116
:
Poly (lactic-co-glycolic acid) (PLGA) porous scaffold for tissue engineering. Enlargement of a Pore. Average Pore Size 350-550 mm, porosity estimated at 35-45% System: Poly (lactic-co-glycolic acid) (PLGA), Composition: Not specified Scanning electron microscopy (SEM) 250 μm |
![]() |
Micrograph
117
:
Sintered disc of Hydroxyapatite (Ca10(PO4)6(OH)2), a calcium phosphate ceramic with similar composition to natural bone mineral System: Hydroxyapatite (Ca10(PO4)6(OH)2), Composition: Not specified Scanning electron microscopy (SEM) 18 μm |
![]() |
Micrograph
118
:
Poly (lactic-co-glycolic acid) (PLGA) porous scaffold for tissue engineering. Average Pore Size 100-300 µm, porosity estimated at 65% System: Poly (lactic-co-glycolic acid) (PLGA), Composition: Not specified Scanning electron microscopy, environmental 400 μm |