64 micrographs for system Cu-Zn, ordered by micrograph number.
Showing 21 - 30 of 64 micrographs | Page 1 2 3 4 5 6 7 | Previous | Next |
![]() |
Micrograph
426
:
Cu 70, Zn 30 (wt%) (pure) brass, dendritic solidification System: Cu-Zn, Composition: Cu 70, Zn 30 (wt%) (pure) Reflected light microscopy 400 μm |
![]() |
Micrograph
427
:
Cu 70, Zn 30 (wt%), recrystallised - annealing twins System: Cu-Zn, Composition: Cu 70, Zn 30 (wt%) Reflected light microscopy 400 μm |
![]() |
Micrograph
428
:
Cu 70, Zn 30 (wt%), recrystallised - annealing twins System: Cu-Zn, Composition: Cu 70, Zn 30 (wt%) Reflected light microscopy 200 μm |
![]() |
Micrograph
429
:
Cu 70, Zn 30 (wt%), recrystallised - annealing twins System: Cu-Zn, Composition: Cu 70, Zn 30 (wt%) Reflected light microscopy 400 μm |
![]() |
Micrograph
430
:
Cu 70, Zn 30 (wt%), recrystallised - annealing twins System: Cu-Zn, Composition: Cu 70, Zn 30 (wt%) Reflected light microscopy 100 μm |
![]() |
Micrograph
431
:
Cu 80, Zn 20 (wt%), recrystallised - annealing twins System: Cu-Zn, Composition: Cu 80, Zn 20 (wt%) Reflected light microscopy 400 μm |
![]() |
Micrograph
432
:
Cu 80, Zn 20 (wt%), recrystallised - annealing twins System: Cu-Zn, Composition: Cu 80, Zn 20 (wt%) Reflected light microscopy 200 μm |
![]() |
Micrograph
433
:
Cu 90, Zn 10 (wt%), recrystallised - annealing twins System: Cu-Zn, Composition: Cu 90, Zn 10 (wt%) Reflected light microscopy 400 μm |
![]() |
Micrograph
434
:
Cu 90, Zn 10 (wt%), recrystallised - annealing twins System: Cu-Zn, Composition: Cu 90, Zn 10 (wt%) Reflected light microscopy 200 μm |
![]() |
Micrograph
439
:
a b nickel brass containing 2% lead. System: Cu-Zn, Composition: Cu 46, Zn 42, Ni 10, Pb 2 (wt%) Reflected light microscopy 800 μm |