Categories > Metal or alloy > Cu-Zn > Reflected light microscopy > Keyword: dendrite
17 micrographs available, ordered by micrograph number.
Showing 1 - 10 of 17 micrographs | Page 1 2 | Previous | Next |
Micrograph
420
:
Commercial brass, ~30% Zn, displaying dendritic solidification System: Cu-Zn, Composition: Cu 70, Zn 30 (approx), Pb 1.3, Sn 0.5-1.0 (wt%) Reflected light microscopy 800 μm |
|
Micrograph
421
:
Commercial brass, ~30% Zn, displaying dendritic solidification System: Cu-Zn, Composition: Cu 70, Zn 30 (approx), Pb 1.3, Sn 0.5-1.0 (wt%) Reflected light microscopy 400 μm |
|
Micrograph
422
:
Commercial brass, ~30% Zn, displaying dendritic solidification System: Cu-Zn, Composition: Cu 70, Zn 30 (approx), Pb 1.3, Sn 0.5-1.0 (wt%) Reflected light microscopy 800 μm |
|
Micrograph
423
:
Commercial brass, ~30% Zn, displaying dendritic solidification System: Cu-Zn, Composition: Cu 70, Zn 30 (approx), Pb 1.3, Sn 0.5-1.0 (wt%) Reflected light microscopy 400 μm |
|
Micrograph
424
:
Commercial brass, ~30% Zn, displaying dendritic solidification System: Cu-Zn, Composition: Cu 70, Zn 30 (approx), Pb 1.3, Sn 0.5-1.0 (wt%) Reflected light microscopy 200 μm |
|
Micrograph
425
:
Cu 70, Zn 30 (wt%) (pure) brass, dendritic solidification System: Cu-Zn, Composition: Cu 70, Zn 30 (wt%) (pure) Reflected light microscopy 800 μm |
|
Micrograph
426
:
Cu 70, Zn 30 (wt%) (pure) brass, dendritic solidification System: Cu-Zn, Composition: Cu 70, Zn 30 (wt%) (pure) Reflected light microscopy 400 μm |
|
Micrograph
447
:
Cu 65, Zn 35 (wt%) B4 brass, chill cast System: Cu-Zn, Composition: Cu 65, Zn 35 (wt%) (pure) Reflected light microscopy 400 μm |
|
Micrograph
448
:
Cu 65, Zn 35 (wt%) B4 brass, chill cast System: Cu-Zn, Composition: Cu 65, Zn 35 (wt%) (pure) Reflected light microscopy 200 μm |
|
Micrograph
468
:
Cu 50, Zn 50 (wt%) brass, as cast System: Cu-Zn, Composition: Cu 50, Zn 50 (wt%) Reflected light microscopy 800 μm |
Showing 1 - 10 of 17 micrographs | Page 1 2 | Previous | Next |