Contributor
44 micrographs contributed by Dr K M Knowles, ordered by micrograph number.
Showing 31 - 40 of 44 micrographs | Page 1 2 3 4 5 | Previous | Next |
Micrograph
543
:
Devitrified Glass: glass sample heated at 900°C for 17 hours System: SiO2, Composition: Mostly silica, SiO2 Transmitted polarised light microscopy, with sensitive tint plate 250 μm |
|
Micrograph
544
:
Devitrified Glass: glass sample heated at 900°C for 17 hours System: SiO2, Composition: Mostly silica, SiO2 Transmitted polarised light microscopy, with sensitive tint plate 250 μm |
|
Micrograph
545
:
Fibre reinforced magnesium aluminosilicate ceramic showing black areas of porosity System: SiC fibre-reinforced magnesium aluminosilicate, Composition: Not specified Reflected light microscopy 100 μm |
|
Micrograph
546
:
Delamination cracks seen in h-BN particles subjected to compressive stress in the (0001) planes (within a silicon nitride particulate-reinforced silicon carbide composite) System: Si3N4-SiC composite, Composition: Not specified High resolution electron microscopy (HREM) 10 nm |
|
Micrograph
547
:
h-BN inclusion (precipitate) in a b-Si3N4 grain (within a silicon nitride particulate-reinforced silicon carbide composite) System: Si3N4-SiC composite, Composition: Not specified High resolution electron microscopy (HREM) 20 nm |
|
Micrograph
548
:
Fractograph showing extensive matrix cracking and fibres bridging an opened matrix in a fibre reinforced magnesium aluminosilicate ceramic System: SiC fibre-reinforced magnesium aluminosilicate, Composition: Not specified Scanning electron microscopy (SEM) 200 μm |
|
Micrograph
549
:
Misoriented interphase boundary between h-BN (precipitate) and SiC grains (within a silicon nitride particulate-reinforced silicon carbide composite) System: Si3N4-SiC composite, Composition: Not specified High resolution electron microscopy (HREM) 1.2 nm |
|
Micrograph
550
:
Micrograph showing the complex chemical reactions which arise at fibre-matrix interfaces in a fibre reinforced magnesium aluminosilicate ceramic subjected to oxidation System: SiC fibre-reinforced magnesium aluminosilicate, Composition: Not specified Bright-field TEM 300 nm |
|
Micrograph
551
:
A regularly stepped interface boundary between h-BN (precipitate) and Si3N4 grains (within a silicon nitride particulate-reinforced silicon carbide composite) System: Si3N4-SiC composite, Composition: Not specified High resolution electron microscopy (HREM) 10 nm |
|
Micrograph
552
:
An amorphous phase trapped at a triple junction between Si3N4 grains (within a silicon nitride particulate-reinforced silicon carbide composite). System: Si3N4-SiC composite, Composition: Not specified High resolution electron microscopy (HREM) 20 nm |
Showing 31 - 40 of 44 micrographs | Page 1 2 3 4 5 | Previous | Next |