Micrograph 786 and full record
- Micrograph no
- 786
- Brief description
- Austempered ductile cast iron
- Keywords
- alloy , austempering , carbon, cast iron , copper, ductile , ferrite , graphite , iron, manganese, metal, molybdenum, pearlite , silicon
- Categories
- Metal or alloy
- System
- Fe-C-X
- Composition
- Fe, C 3.52, Si 2.51, Mn 0.49, Mo 0.15, Cu 0.31 (wt%)
- Standard codes
- Reaction
- Processing
- Applications
- Sample preparation
- Etchant: Nital 2%
- Technique
- Reflected light microscopy
- Length bar
- 100 μm
- Further information
- Austenitised at 950°C, austempered at 400°C for 52 min.
Source: http://www.msm.cam.ac.uk/phase-trans/2001/adi/adimore.html. - Contributor
- Dr M A Yescas-Gonzalez
- Organisation
- Department of Materials Science and Metallurgy, University of Cambridge
- Date
- 18/07/03
- Licence for re-use
- DoITPoMS standard terms of use
- Related micrographs
- Micrograph 782: Austempered ductile cast iron (100 μm)
- Micrograph 783: Austempered ductile cast iron (100 μm)
- Micrograph 784: Austempered ductile cast iron (100 μm)
- Micrograph 785: Austempered ductile cast iron (20 μm)
- Micrograph 787: Austempered ductile cast iron (20 μm)
- Micrograph 788: Austempered ductile cast iron (100 μm)
- Micrograph 789: Austempered ductile cast iron (40 μm)
- Micrograph 790: Austempered ductile cast iron (20 μm)
- Micrograph 791: Austempered ductile cast iron (100 μm)
- Micrograph 792: Austempered ductile cast iron (20 μm)
- Micrograph 793: Austempered ductile cast iron (100 μm)
- Micrograph 794: Austempered ductile cast iron (20 μm)
View image alone .. in a new window
Help is available on downloading images