8 videos for category SEM:


Image Link to full record for video 53 video 53 : SEM video of the appearance of slip steps as slip begins on a previously undeformed single crystal of cadmium. From TLP: Slip in Single Crystals
Image Link to full record for video 54 video 54 : Longer version of video 53 - SEM video of the appearance of slip steps as slip begins on a previously undeformed single crystal of cadmium. From TLP: Slip in Single Crystals
Image Link to full record for video 55 video 55 : SEM video of a single cadmium crystal fracturing under tensile load. The mode of fracture is ductile tearing. Shows how the angle of the fracture surfaces mimics the angle of the slip planes in the deformed crystal. From TLP: Slip in Single Crystals
Image Link to full record for video 56 video 56 : Slip proceeding on previously deformed single cadmium crystal fracturing in an SEM. The trace of the slip planes can be seen. Markers have been dropped onto the surface of the crystal to allow the relative movement of parts of the crystal to be clearly seen. From TLP: Slip in Single Crystals
Image Link to full record for video 57 video 57 : Slip proceeding on previously deformed single cadmium crystal. An unusually large slip step can be seen on the left-hand edge of the specimen. As slip proceeds, the slip planes rotate towards the tensile axis, but the large slip step does not increase in size. From TLP: Slip in Single Crystals
Image Link to full record for video 87 video 87 : Hillock growth in conductor lines as a result of electromigration. From TLP Electromigration
Image Link to full record for video 88 video 88 : Void growth on a sputtered surface as a result of electromigration. From TLP Electromigration
Image Link to full record for video 89 video 89 : Void growth on Al line through HVSEM TLP Electromigration